Title:Temperature- and Field Dependent Characterization of a Twisted Stacked-Tape Cable
View PDFAbstract:The Twisted Stacked-Tape Cable (TSTC) is one of the major high temperature superconductor cable concepts combining scalability, ease of fabrication and high current density making it a possible candidate as conductor for large scale magnets. To simulate the boundary conditions of such a magnets as well as the temperature dependence of Twisted Stacked-Tape Cables a 1.16 m long sample consisting of 40, 4 mm wide SuperPower REBCO tapes is characterized using the "FBI" (force - field - current) superconductor test facility of the Institute for Technical Physics (ITEP) of the Karlsruhe Institute of Technology (KIT). In a first step, the magnetic background field is cycled while measuring the current carrying capabilities to determine the impact of Lorentz forces on the TSTC sample performance. In the first field cycle, the critical current of the TSTC sample is tested up to 12 T. A significant Lorentz force of up to 65.6 kN/m at the maximal magnetic background field of 12 T result in a 11.8 % irreversible degradation of the current carrying capabilities. The degradation saturates (critical cable current of 5.46 kA at 4.2 K and 12 T background field) and does not increase in following field cycles. In a second step, the sample is characterized at different background fields (4-12 T) and surface temperatures (4.2-37.8 K) utilizing the variable temperature insert of the "FBI" test facility. In a third step, the performance along the length of the sample is determined at 77 K, self-field. A 15 % degradation is obtained for the central part of the sample which was within the high field region of the magnet during the in-field measurements.
Current browse context:
cond-mat.supr-con
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.